DIMENSIONAL CHANGES IN THE MOULDING
INFLUENCE OF PROCESS ON SHRINKAGE
MATERIALS, MOULD AND PROCESS CONDITIONS INFLUENCE SHRINKAGE.
|
SHRINKAGE DECREASES with |
SHRINKAGE INCREASES with |
MATERIALS |
AMORPHOUS REINFORCED |
CRYSTALLINE HIGHER WALL THICKNESS |
MOULD |
HIGH CONDUCTIVITY STEEL |
LONG FLOW PATH SMALL GATE AREA INSUFFICIENT COOLING INSUFFICIENT CLAMP FORCE |
PROCESS CONDITION |
|
|
HIGH CAVITY PRESSURE HIGH INJECTION RATE |
HIGH MOULD TEMPERATURE INSUFFICIENT GATE FREEZE-OFF TIME HIGH MELT TEMPERATURE |
SHRINKAGE OF VARIOUS MATERIALS
MATERIALS |
% SHRINKAGE |
MATERIALS |
% SHRINKAGE |
Nylon 6 |
1 -1.5 |
Polycarbonate |
0.8 |
Nylon 6- GR |
0.5 |
Acetal |
2 |
Nylon 6/6 |
1 -2 |
PVC - Rigid |
0.5 - 0.7 |
Nylon 6/6 -GR |
0.5 |
PVC - Soft |
1 - 3 |
LDPE |
1.5 - 3 |
ABS |
0.4 - 0.6 |
HDPE |
2 - 3 |
PP |
1.2 - 2 |
Polystyrene |
0.5 - 0.7 |
Cellulose acetate |
0.5 |
Styrene-acrylonitrile |
0.4 - 0.6 |
Cellulose acetate.......... butyrate |
0.5 |
Acrylic |
0.3 - 0.6 |
Cellulose propionate |
0.5 |
|
|
|
|